- Code
- AS1810
- Sub Group
- None Feature
- Feature 1
- Non-Corrosive
- Feature 2
- Excellent adhesion to most substrates
- Feature 3
- Improved fuel resistance
- Feature 4
- Cure through to 3 mm in 24 hours
- Old Code
- ESP411
- Appearance
- Paste
- Test Conditions
- After 7 days cure at 23°+/-2°C and 50+/-5% humidity
- Colour
- Black
- SG
- 1.05
- Min Working Temp - °C
- -50 °C
- Max Working Temp +°C
- 220 °C
- FDA
- No
- Shelf life
- 12 mths
- Max storage temperature °C
- 40 °C
- Pack Type
- 1-Part
- Rheology
- Paste
- Non Corrosive
- Yes
- Cure Type
- Acetone
- RTV or Heat cure
- RTV
- Self Bonding
- Yes
- UL 94V-0
- No
- Duro Shore A
- 35
- Tensile MPa
- 1.81 MPa
- Elongation %
- 353 %
- Tear kN/m
- 6 kN/m
- Extrusion Rate g/min
- 169 g/min
- Modulus Youngs MPa
- 0.5 MPa
- Modulus @ 100% Strain MPa
- 0.8 MPa
- Linear Shrinkage %
- 0.4 %
- CTE Volumetric ppm/°C
- 884 ppm/°C
- CTE Linear ppm/°C
- 295 ppm/°C
- Tack Free Time mins
- 4 mins
- Max Cure Hrs @ 25 °C
- 24 hrs
- Thermal Conductivity W/mK
- 0.19 W/mK
- Volume Resistivity ohms cm
- 6.38E+14 ohms cm
- Surface Resistivity ohms
- 3.3E+12 ohms
- Dielectric Strength kV/mm
- >20 kV/mm
- Dielectric Constant @ 1kHz
- 2.97
- Dissipation Factor @ 1kHz
- 0.0025
- Lap Shear Copper kg/cm²
- 4.87 kg/cm²
- Lap Shear Aluminium kg/cm²
- 6.94 kg/cm²