Silcoset 101


Downloads Request Sample
TDS
SDS
Description
2 Part condensation cure silicone encapsulant high temperature
Feature
  • High temperature resistance
  • Rolls Royce Aerospace approved
  • Ideal for low melt metal alloy casting
  • Good flow properties
Code
Silcoset 101
Sub Group
None
Feature
Feature 1
High temperature resistance
Feature 2
Rolls Royce Aerospace approved
Feature 3
Ideal for low melt metal alloy casting
Feature 4
Good flow properties
Old Code
Silcoset 101
Appearance
Viscous Liquid
Test Conditions
After 7 days cure at 23°+/-2°C and 60+/-5% humidity
Colour
Red
Colour A Part
Red
Colour B Part
Clear
SG
1.5
SG A Part
~1
SG B Part
~1
Min Working Temp - °C
-60 °C
Max Working Temp +°C
250 °C
FDA
No
Shelf life
7 mths
Max storage temperature °C
30 °C
Pack Type
2-Part Kit
Mix Ratio
100:1
Rheology
Viscous Liquid
Viscosity A-Part mPas
45000 mPas
Viscosity B-Part mPas
300 mPas
Viscosity Mixed mPas
40000 mPas
Non Corrosive
Yes
Cure Type
Condensation
RTV or Heat cure
RTV
Self Bonding
No
UL 94V-0
No
Duro Shore A
61
Tensile MPa
4.77 MPa
Elongation %
131 %
Tear kN/m
8.1 kN/m
Modulus @ 100% Strain MPa
4.18 MPa
Linear Shrinkage %
0.41 %
CTE Volumetric ppm/°C
708 ppm/°C
CTE Linear ppm/°C
236 ppm/°C
Max Cure Hrs @ 25 °C
4 hrs
Thermal Conductivity W/mK
0.37 W/mK
Volume Resistivity ohms cm
1.51E+14 ohms cm
Dielectric Strength kV/mm
20 kV/mm
Power Factor @1MHz
0.0025
Permittivity
3
Pot Life mins
60 mins