- Code
- Silcoset 152
- Sub Group
- None Feature
- Feature 1
- Flexible from - 60 to +300°C
- Feature 2
- Rolls Royce Aerospoace approved
- Feature 3
- Good electrical insulation
- Feature 4
- Excellent adhesion to most substrates
- Old Code
- Silcoset 152
- Appearance
- White paste
- Test Conditions
- After 7 days cure at 23°+/-2°C and 60+/-5% humidity
- Colour
- White
- SG
- 1.08
- Min Working Temp - °C
- -60 °C
- Max Working Temp +°C
- 300 °C
- FDA
- No
- Shelf life
- 24 mths
- Max storage temperature °C
- 40 °C
- Pack Type
- 1-Part
- Rheology
- Paste
- Non Corrosive
- No
- Cure Type
- Acetoxy
- RTV or Heat cure
- RTV
- Self Bonding
- Yes
- UL 94V-0
- No
- Duro Shore A
- 40
- Hardness IRHD
- 40
- Tensile MPa
- 2.31 MPa
- Elongation %
- 240 %
- Tear kN/m
- 6.1 kN/m
- Extrusion Rate g/min
- 225 g/min
- Compression Set %
- 40 %
- Modulus Youngs MPa
- 0.75 MPa
- Modulus @ 100% Strain MPa
- 1 MPa
- Linear Shrinkage %
- 1 %
- CTE Volumetric ppm/°C
- 876 ppm/°C
- CTE Linear ppm/°C
- 292 ppm/°C
- Tack Free Time mins
- 2 mins
- Max Cure Hrs @ 25 °C
- 7 hrs
- Thermal Conductivity W/mK
- 0.2 W/mK
- Volume Resistivity ohms cm
- 3.21E+15 ohms cm
- Surface Resistivity ohms
- 3.46E+14 ohms
- Dielectric Constant @ 1kHz
- 3.6
- Dissipation Factor @ 1kHz
- 0.008
- Lap Shear Aluminium kg/cm²
- 10.6 kg/cm²